Inorganic and organic nitrate additives for nonaqueous electrolyte in alkali metal electrochemical cells

ABSTRACT

An alkali metal, solid cathode, nonaqueous electrochemical cell capable of delivering high current pulses, rapidly recovering its open circuit voltage and having high current capacity, is described. The stated benefits are realized by the addition of at least one nitrate additive to an electrolyte comprising an alkali metal salt dissolved in a mixture of a low viscosity solvent and a high permittivity solvent. A preferred solvent mixture includes propylene carbonate, dimethoxyethane and an alkali metal nitrate, alkaline earth metal nitrate and/or an organic alkyl nitrate additive.

BACKGROUND OF INVENTION

1. Field of the Invention

The present invention generally relates to an alkali metal electrochemical cell, and more particularly, to an alkali metal cell suitable for current pulse discharge applications with improved discharge performance. Still more particularly, the present invention relates to a lithium electrochemical cell activated with an electrolyte having an additive for the purpose of providing increased discharge voltages and reducing and/or eliminating voltage delay under current pulse discharge applications. Voltage delay is a phenomenon typically exhibited in an alkali metal/transition metal oxide cell, and particularly, a lithium/silver vanadium oxide cell, that has been depleted of 40% to 70% of its capacity and is subjected to current pulse discharge applications. According to the present invention, the preferred additive to the activating electrolyte for such a chemistry is an alkali metal nitrate and/or an organic alkyl nitrate compound.

The voltage response of a cell which does not exhibit voltage delay during the application of a short duration pulse or pulse train has distinct features. First, the cell potential decreases throughout the application of the pulse until it reaches a minimum at the end of the pulse, and second, the minimum potential of the first pulse in a series of pulses is higher than the minimum potential of the last pulse.

On the other hand, the voltage response of a cell which exhibits voltage delay during the application of a short duration pulse or during a pulse train can take one or both of two forms. One form is that the leading edge potential of the first pulse is lower than the end edge potential of the first pulse. In other words, the voltage of the cell at the instant the first pulse is applied is lower than the voltage of the cell immediately before the first pulse is removed. The second form of voltage delay is that the minimum potential of the first pulse is lower than the minimum potential of the last pulse when a series of pulses have been applied.

The initial drop in cell potential during the application of a short duration pulse reflects the resistance of the cell, i.e., the resistance due to the cathode, the cathode-electrolyte interphase, the anode and the anode-electrolyte interphase. In the absence of voltage delay, the resistance due to passivated films on the anode and/or cathode is negligible. However, the formation of a surface film is unavoidable for alkali metal, and in particular, lithium metal anodes, and for lithium intercalated carbon anodes, due to their relatively low potential and high reactivity towards organic electrolytes. Thus, the ideal anode surface film should be electrically insulating and ionically conducting. While most alkali metal, and in particular, lithium electrochemical systems meet the first requirement, the second requirement is difficult to achieve. In the event of voltage delay, the resistance of these films is not negligible, and as a result, impedance builds up inside the cell due to this surface layer formation which often results in reduced discharge voltage and reduced cell capacity. In other words, the drop in potential between the background voltage and the lowest voltage under pulse discharge conditions, excluding voltage delay, is an indication of the conductivity of the cell, i.e., the conductivity of the cathode, anode, electrolyte, and surface films, while the gradual decrease in cell potential during the application of the pulse train is due to the polarization of the electrodes and electrolyte.

Thus, decreased discharge voltages and the existence of voltage delay are undesirable characteristics of alkali metal/mixed metal oxide cells subjected to current pulse discharge conditions in terms of their influence on devices such as medical devices including implantable pacemakers and cardiac defibrillators. Depressed discharge voltages and voltage delay are undesirable because they limit the effectiveness and even the proper functioning of both the cell and the associated electrically powered device under current pulse discharge conditions.

2. Prior Art

One of the known solutions to the above problems is to saturate the electrolyte solution with carbon dioxide CO₂. Cycling efficiency is improved dramatically in secondary cell systems having a lithium anode activated with CO₂ saturated electrolytes (V. R. Koch and S. B. Brummer, Electrochimica Acta, 1978, 23, 55-62; U.S. Pat. No. 4,853,304 to Ebner et al.; D. Aurbach, Y. Gofer, M. Ben-Zion and P. Aped, J. Electroanal. Chem. 1992, 339, 451-471). U.S. Pat. No. 5,569,558 to Takeuchi et al. relates to the provision of a CO₂ saturated electrolyte for alleviating the presence of voltage delay in primary cells having a mixed transition metal oxide cathode such as lithium/silver vanadium oxide cells. The same effect is also known for lithium intercalated carbon anode secondary batteries (D. Aurbach, Y. Ein-Eli, O. Chusid, Y. Carmeli, M. Babai and H. Yamin, J. Electrochem. Soc. 1994, 141, 603-611). Sulfur dioxide (SO₂) has also been reported to be another additive that improves charge-discharge cycling in rechargeable lithium ion cells (Y. Ein-Eli, S.R. Thomas and V. R. Koch, J. Electrochem. Soc. 1996, 143, L195-L197).

In spite of the success of CO₂ and SO₂ in improving cell discharge characteristics, their use has been limited. One problem associated with both CO₂ and SO₂ as electrolyte additives is that they are in a gaseous state at room temperature, and are thus difficult to handle. Also, it is difficult to control the dissolved concentration of CO₂. Best results are achieved at pressures of up to 50 psig., which further detracts from the practicality of this additive.

Instead of carbon dioxide and sulfur dioxide, the present invention is directed to the provision of nitrate additives in the electrolyte of an alkali metal electrochemical cell to beneficially modify the anode surface film. The nitrate additives are defined herein as an alkali metal nitrate, an alkaline earth metal nitrate and/or organic alkyl nitrate compounds provided as a co-solvent with commonly used organic aprotic solvents. The nitrate additives are in a condensed phase which makes them easy to handle in electrolyte preparation. When used as a co-solvent in an activating electrolyte, the nitrite additives interact with the alkali metal anode to form an ionically conductive surface protective layer thereon. The conductive surface layer improves the discharge performance of the alkali metal electrochemical cell by providing increased discharge voltages and minimizing or even eliminating voltage delay in the high current pulse discharge of such cells.

SUMMARY OF THE INVENTION

The object of the present invention is to improve the pulse discharge performance of an alkali metal electrochemical cell and, more particularly, a primary lithium electrochemical cell, by the provision of at least one nitrate additive, preferably an alkali metal nitrate, and alkaline earth metal nitrate and/or an organic alkyl nitrate compound as a co-solvent in the cell's activating nonaqueous electrolyte solution. Due to the high reduction potential of the nitrate group vs. lithium, the nitrate additives compete effectively with the other electrolyte co-solvents or the solute to react with the lithium anode. Lithium nitrate or the lithium salt of nitrate reduction products are believed to be the major reaction products. These lithium salts are believed to deposit on the anode surface to form an ionically conductive protective film thereon. As a consequence, the chemical composition and perhaps the morphology of the anode surface protective layer is changed, and this proves beneficial to the discharge characteristics of the cell.

The thusly fabricated cell exhibits higher discharge potentials and improved voltage delay under current pulse discharge usage, which is an unexpected result. More particularly, the present invention is directed to the introduction of at least one nitrate additive into the electrolyte of a lithium/silver vanadium oxide electrochemical cell for the purpose of improving the pulse minimum potentials and reducing and/or eliminating voltage delay during pulse discharging applications. Alkali metal/transition metal oxide electrochemical systems are typically activated with an electrolyte comprising a relatively low viscosity solvent and a relatively high permittivity solvent. The solute of the electrolyte is an inorganic alkali metal salt wherein the alkali metal of the salt is the same as the alkali metal of the anode. The nitrate compounds of the present invention are introduced into the electrolyte as an additive to interact with the alkali metal anode, and particularly with the lithium anode, to form an ionically conductive protective anode surface layer which improves the discharge performance of the cell through higher discharge potentials under current pulse discharge conditions. Therefore, the present invention is directed to a novel electrolyte solution provided in operative association with an electrochemical system incorporated into a defibrillator battery to improve discharge performance under high current pulse discharge conditions.

These and other objects of the present invention will become increasingly more apparent to those skilled in the art by reference to the following description and to the appended drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 and 5 are graphs constructed from the pulse train 5 waveforms of Li/SVO cells activated with a nonaqueous electrolyte devoid of lithium nitrate and having various concentrations of that additive dissolved therein.

FIGS. 6 to 11 are graphs constructed from the pulse train 5 waveforms of Li/SVO cells activated with a nonaqueous electrolyte devoid of isopropyl nitrate and various concentrations of that additive dissolved therein.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

As used herein, the term "pulse" means a short burst of electrical current of a significantly greater amplitude than that of a prepulse current immediately prior to the pulse. A pulse train consists of at least two pulses of electrical current delivered in relatively short succession with or without open circuit rest between the pulses.

The electrochemical cell of the present invention includes an anode selected from Groups IA, IIA or IIIB of the Periodic Table of Elements, including lithium, sodium, potassium, etc., and their alloys and intermetallic compounds including, for example Li--Si, Li--B and Li--Si--B alloys and intermetallic compounds. The preferred anode comprises lithium, and the more preferred anode comprises a lithium alloy, the preferred lithium alloy being a lithium-aluminum alloy. The greater the amount of aluminum present by weight in the alloy, however, the lower the energy density of the cell.

The form of the anode may vary, but preferably the anode is a thin metal sheet or foil of the anode metal, pressed or rolled on a metallic anode current collector, i.e., preferably comprising nickel, to form an anode component. In the exemplary cell of the present invention, the anode component has an extended tab or lead of the same material as the anode current collector, i.e., preferably nickel, integrally formed therewith such as by welding and contacted by a weld to a cell case of conductive metal in a case-negative electrical configuration. Alternatively, the anode may be formed in some other geometry, such as a bobbin shape, cylinder or pellet to allow an alternate low surface cell design.

The cathode is preferably of a solid material and the electrochemical reaction at the cathode involves conversion of ions which migrate from the anode to the cathode in atomic or molecular forms. The solid cathode material may comprise a metal, a metal oxide, a mixed metal oxide, a metal sulfide or a carbonaceous compound, and combinations thereof. The metal oxide, the mixed metal oxide and the metal sulfide can be formed by the chemical addition, reaction, or otherwise intimate contact of various metal oxides, metal sulfides and/or metal elements, preferably during thermal treatment, sol-gel formation, chemical vapor deposition or hydrothermal synthesis in mixed states. The active materials thereby produced contain metals, oxides and sulfides of Groups IB, IIB, IIIB, IVB, VB, VIB, VIIB and VIII, which includes the noble metals and/or other oxide and sulfide compounds.

One preferred mixed metal oxide has the general formula SM_(x) V₂ O_(y) wherein SM is a metal selected from Groups IB to VIIB and VIII of the Periodic Table of Elements, wherein x is about 0.30 to 2.0 and y is about 4.5 to 6.0 in the general formula. By way of illustration, and in no way intended to be limiting, one exemplary cathode active material comprises silver vanadium oxide (SVO) having the general formula Ag_(x) V₂ O_(y) in any one of its many phases, i.e., β-phase silver vanadium oxide having in the general formula x=0.35 and y=5.8, γ-phase silver vanadium oxide having in the general formula x=0.74 and y=5.37 and ε-phase silver vanadium oxide having in the general formula x=1.0 and y=5.5, and combination and mixtures of phases thereof. For a more detailed description of such a cathode active material, reference is made to U.S. Pat. No. 4,310,609 to Liang et al., which is assigned to the assignee of the present invention and incorporated herein by reference.

Another preferred composite cathode active material includes V₂ O_(z) wherein z≧5 combined with Ag₂ O with the silver in either the silver(II), silver(I) or silver(0) oxidation state and CuO with the copper in either the copper(II), copper(I) or copper(O) oxidation state to provide the mixed metal oxide having the general formula Cu_(x) Ag_(y) V₂ O_(z), (CSVO). Thus, this composite cathode active material may be described as a metal oxide-metal oxide-metal oxide, a metal-metal oxide-metal oxide, or a metal-metal-metal oxide and the range of material compositions found for Cu_(x) Ag_(y) V₂ O_(z) is preferably about 0.01≧x≧1.0, about 0.01≧y≧1.0 and about 5.01≧z≧6.5. Typical forms of CSVO are Cu₀.16 Ag₀.67 V₂ O_(z) with z being about 5.5 and Cu₀.5 Ag₀.5 V₂ O_(z), with z being about 5.75. The oxygen content is designated by z since the exact stoichiometric proportion of oxygen in CSVO can vary depending on whether the cathode material is prepared in an oxidizing atmosphere such as air or oxygen, or in an inert atmosphere such as argon, nitrogen and helium. For a more detailed description of this cathode active material, reference is made to U.S. Pat. No. 5,472,810 to Takeuchi et al. and U.S. Pat. No. 5,516,340 to Takeuchi et al., both of which are assigned to the assignee of the present invention and incorporated herein by reference.

Additional cathode active materials include manganese dioxide, lithium cobalt oxide, lithium nickel oxide, copper vanadium oxide, titanium disulfide, copper oxide, copper sulfide, iron sulfide, iron disulfide, and fluorinated carbon, and mixtures thereof. Preferably, the cathode comprises from about 80 to about 99 weight percent of the cathode active material.

Cathode active materials prepared as described above are preferably mixed with a binder material such as a powdered fluoro-polymer, more preferably powdered polytetrafluoroethylene or powdered polyvinylidene fluoride present at about 1 to about 5 weight percent of the cathode mixture. Further, up to about 10 weight percent of a conductive diluent is preferably added to the cathode mixture to improve conductivity. Suitable materials for this purpose include acetylene black, carbon black and/or graphite or a metallic powder such as powdered nickel, aluminum, titanium and stainless steel. The preferred cathode active mixture thus includes a powdered fluoro-polymer binder present at about 3 weight percent, a conductive diluent present at about 3 weight percent and about 94 weight percent of the cathode active material. The cathode active mixture may be in the form of one or more plates operatively associated with at least one or more plates of anode material, or in the form of a strip wound with a corresponding strip of anode material in a structure similar to a "jellyroll".

In order to prevent internal short circuit conditions, the cathode is separated from the Group IA, IIA or IIIB anode material by a suitable separator material. The separator is of electrically insulative material, and the separator material also is chemically unreactive with the anode and cathode active materials and both chemically unreactive with and insoluble in the electrolyte. In addition, the separator material has a degree of porosity sufficient to allow flow therethrough of the electrolyte during the electrochemical reaction of the cell. Illustrative separator materials include woven and non-woven fabrics of polyolefinic fibers or fluoropolymeric fibers including polyvinylidene fluoride, polyethylenetetrafluoro-ethylene, and polyethylenechlorotrifluoroethylene laminated or superposed with a polyolefinic or a fluoropolymeric microporous film. Suitable microporous films include a polytetrafluoro-ethylene membrane commercially available under the designation ZITEX (Chemplast Inc.), polypropylene membrane commercially available under the designation CELGARD (Celanese Plastic Company, Inc.) and a membrane commercially available under the designation DEXIGLAS (C. H. Dexter, Div., Dexter Corp.). The separator may also be composed of non-woven glass, glass fiber materials and ceramic materials.

The form of the separator typically is a sheet which is placed between the anode and cathode electrodes and in a manner preventing physical contact therebetween. Such is the case when the anode is folded in a serpentine-like structure with a plurality of cathode plates disposed intermediate the anode folds and received in a cell casing or when the electrode combination is rolled or otherwise formed into a cylindrical "jellyroll" configuration.

The electrochemical cell of the present invention further includes a nonaqueous, ionically conductive electrolyte operatively associated with the anode and the cathode electrodes. The electrolyte serves as a medium for migration of ions between the anode and the cathode during the electrochemical reactions of the cell and nonaqueous solvents suitable for the present invention are chosen so as to exhibit those physical properties necessary for ionic transport (low viscosity, low surface tension and wettability). Suitable nonaqueous solvents are comprised of an inorganic salt dissolved in a nonaqueous solvent and more preferably an alkali metal salt dissolved in a mixture of aprotic organic solvents comprising a low viscosity solvent including organic esters, ethers and dialkyl carbonates, and mixtures thereof, and a high permittivity solvent including cyclic carbonates, cyclic esters and cyclic amides, and mixtures thereof. Low viscosity solvents include tetrahydrofuran (THF), methyl acetate (MA), diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane (DME), 1,2-diethoxyethane (DEE), 1-ethoxy, 2-methoxyethane (EME), dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), ethyl methyl carbonate (EMC), methyl propyl carbonate (MPC) and ethyl propyl carbonate (EPC), and mixtures thereof. High permittivity solvents include propylene carbonate (PC), ethylene carbonate (EC), butylene carbonate (BC), acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-butyrolactone (GBL) and N-methyl-pyrrolidinone (NMP), and mixtures thereof.

The preferred electrolyte comprises an inorganic alkali metal salt, and in the case of an anode comprising lithium, the alkali metal salt of the electrolyte is a lithium based salt. Known lithium salts that are useful as a vehicle for transport of alkali metal ions from the anode to the cathode include LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄₁ LiC(SO₂ CF₃)₃, LiN(SO₂ CF₃)₂, LiSCN, LiO₃ SCF₂ CF₃, LiC₆ F₅ SO₃, LiO₂ CCF₃, LiSO₃ F, LiB(C₆ H₅)₄ and LiCF₃ SO₃, and mixtures thereof. Suitable salt concentrations typically range between about 0.8 to 1.5 molar, and a preferred electrolyte for a lithium/transition metal oxide electrochemical cell includes LiAsF₆ or LiPF₆ dissolved in a 50:50 mixture, by volume, of PC and DME.

In accordance with the present invention, at least one organic or inorganic nitrate additive is provided as a co-solvent in the electrolyte solution of the previously described alkali metal electrochemical cell. The nitrate additive is preferably an alkali metal nitrate, an alkaline earth metal nitrate or an organic alkyl nitrate compound having the general formula (RO)N(═O)₂, wherein R is an alkali metal cation, an alkaline metal cation or an organic group of either a saturated or unsaturated hydrocarbon or heteroatom substituted saturated or unsaturated organic group containing 1 to 10 carbon atoms. The greatest effect is found when lithium nitrate, sodium nitrate, potassium nitrate, magnesium nitrate, calcium nitrate, propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof are used as additives in the electrolyte.

The above described compounds are only intended to be exemplary of those that are useful with the present invention, and are not to be construed as limiting. Those skilled in the art will readily recognize nitrate compounds which come under the purview of the general formula set forth above and which will be useful as additives for the electrolyte to reduce voltage delay according to the present invention.

While not intending to be bound by any particular mechanism, it is believed that due to the presence of the two N═O bonds in the nitrate functional group, [--O--N(═O)₂ ], the bond between oxygen and the R group is severed and the nitrate intermediate is able to compete effectively with the other electrolyte solvents or solutes to react with lithium and form a nitrate salt, i.e., lithium nitrate, or the lithium salt of a nitrate reduction product on the surface of the anode. The resulting salt is ionically more conductive than lithium oxide which may form on the anode in the absence of the nitrate additive. As a consequence, the chemical composition and perhaps the morphology of the anode surface protective layer is believed to be changed with concomitant benefits to the cell's discharge characteristics.

In the present invention, the anode is lithium metal and the cathode is preferably the transition mixed metal oxide AgV₂ O₅.5 (SVO). The preferred electrolyte is 1.0M to 1.2M LiAsF₆ dissolved in an aprotic solvent mixture comprising at least one of the above listed low viscosity solvents and at least one of the above listed high permittivity solvents. The preferred aprotic solvent mixture comprises a 50/50, by volume, mixture of propylene carbonate and dimethoxyethane. The concentration of the above discussed nitrate additives according to the present invention should preferably be in the range of between about 0.005M to about 0.01M. The positive effects of these additives in increasing discharge voltages and reducing voltage delay in a pulse discharging alkali metal cell have been achieved both at room temperature as well as at temperatures up to about 37° C. This makes the novel electrolyte solution of the present invention particularly useful for activating an alkali metal/transition metal oxide cell incorporated into an implantable medical device such as a cardiac defibrillator to minimize or even eliminate voltage delay and provide improved minimum potentials under high current pulse discharge conditions.

As is well known by those skilled in the art, an implantable cardiac defibrillator is a device that requires a power source for a generally medium rate, constant resistance load component provided by circuits performing such functions as, for example, the heart sensing and pacing functions. From time to time, the cardiac defibrillator may require a generally high rate, pulse discharge load component that occurs, for example, during charging of a capacitor in the defibrillator for the purpose of delivering an electrical shock to the heart to treat tachyarrhythmias, the irregular, rapid heart beats that can be fatal if left uncorrected. Increased pulse minimum potentials and reduction, and even elimination of voltage delay during a current pulse application is important for proper device operation and extended device life.

The assembly of the cell described herein is preferably in the form of a wound element cell. That is, the fabricated cathode, anode and separator are wound together in a "jellyroll" type configuration or "wound element cell stack" such that the anode is on the outside of the roll to make electrical contact with the cell case in a case-negative configuration. Using suitable top and bottom insulators, the wound cell stack is inserted into a metallic case of a suitable size dimension. The metallic case may comprise materials such as stainless steel, mild steel, nickel-plated mild steel, titanium, tantalum or aluminum, but not limited thereto, so long as the metallic material is compatible for use with components of the cell.

The cell header comprises a metallic disc-shaped body with a first hole to accommodate a glass-to-metal seal/terminal pin feedthrough and a second hole for electrolyte filling. The glass used is of a corrosion resistant type having up to about 50% by weight silicon such as CABAL 12, TA 23 or FUSITE 425 or FUSITE 435. The positive terminal pin feedthrough preferably comprises titanium although molybdenum, aluminum, nickel alloy, or stainless steel can also be used. The cell header comprises elements having compatibility with the other components of the electrochemical cell and is resistant to corrosion. The cathode lead is welded to the positive terminal pin in the glass-to-metal seal and the header is welded to the case containing the electrode stack. The cell is thereafter filled with the electrolyte solution comprising at least one of the nitrate additives described hereinabove and hermetically sealed such as by close-welding a stainless steel ball over the fill hole, but not limited thereto.

The above assembly describes a case-negative cell, which is the preferred construction of the exemplary cell of the present invention. As is well known to those skilled in the art, the exemplary electrochemical system of the present invention can also be constructed in a case-positive configuration.

The following examples describe the manner and process of an electrochemical cell according to the present invention, and set forth the best mode contemplated by the inventors of carrying out the invention, but are not construed as limiting.

EXAMPLE I

Lithium anode material was pressed on nickel current collector screen and silver vanadium oxide cathode material was pressed on titanium current collector screen. A prismatic cell stack assembly configuration with two layers of microporous membrane polypropylene separator sandwiched between the anode and cathode was prepared. The electrode assembly was then hermetically sealed in a stainless steel casing in a case-negative configuration. Three control cells were activated with the standard electrolyte consisting of 1.0M LiAsF₆ dissolved in a 50:50, by volume, mixture of PC and DME without an inorganic or an organic nitrate additive (Group 1). Twelve cells (three cells per group) were activated with the same electrolyte used to activate the Group 1 cells and further containing 0.1M, 0.05M, 0.10M, or 0.20M lithium nitrate (LiNO₃), as set forth in Table 1.

                  TABLE 1                                                          ______________________________________                                         Cell Construction                                                                   Group   [LiAsF.sub.6 ]                                                                               PC:DME [LiNO.sub.3 ]                                ______________________________________                                         1        1.0 M         50:50    0.00 M                                           2 1.0 M 50:50 0.01 M                                                           3 1.0 M 50:50 0.05 M                                                           4 1.0 M 50:50 0.10 M                                                           5 1.0 M 50:50 0.20 M                                                         ______________________________________                                    

A constant resistance load of 3.57 kΩ was applied to all of the cells for 21 hours during an initial predischarge period. The predischarge period is referred to as burn-in and depleted the cells of approximately 1% of their theoretical capacity. Following burn-in, the cells were subjected to acceptance pulse testing consisting of four 10 second pulses (23.2 mA/cm²) with a 15 second rest between each pulse. The average discharge readings for the pre-pulse potentials, voltage delay and pulse minimum potentials during acceptance pulse testing for these pulse trains are summarized in Table 2. Voltage delay is calculated as pulse 1 end potential minus pulse 1 minimum potential.

                  TABLE 2                                                          ______________________________________                                         Acceptance Pulse Train Voltages (average)                                        Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  3.267    0.253  2.290   2.519                                   2 0.01 M 3.267 0.334 2.253 2.537                                               3 0.05 M 3.270 0.338 2.273 2.546                                               4 0.10 M 3.269 0.376 2.222 2.533                                               5 0.20 M 3.266 0.356 2.231 2.515                                             ______________________________________                                    

In the acceptance pulse train, the groups 1 to 5 cells exhibited similar pre-pulse potentials. In addition, all of the cells exhibited voltage delay. Specifically, those cells having the lithium nitrate additive exhibited larger voltage delay relative to that of the group 1 cells.

Following acceptance pulse testing, all of the cells were discharged under loads of 9.53 kohms with superimposed pulse trains applied every 39 days. The pulse trains consisted of four 10 second pulses (23.2 mA/cm²) with 15 seconds rest between each pulse. The average discharge readings for the pre-pulse potentials, voltage delay and pulse minimum potentials for pulse trains 1 to 7 are summarized in Tables 3 to 9, respectively.

                  TABLE 3                                                          ______________________________________                                         Pulse Train 1 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  3.224    0.001  2.619   2.507                                   2 0.01 M 3.222 0.000 2.630 2.528                                               3 0.05 M 3.223 0.000 2.646 2.533                                               4 0.10 M 3.224 0.000 2.626 2.520                                               5 0.20 M 3.224 0.000 2.622 2.504                                             ______________________________________                                    

                  TABLE 4                                                          ______________________________________                                         Pulse Train 2 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  3.156    0.000  2.548   2.430                                   2 0.01 M 3.157 0.000 2.559 2.432                                               3 0.05 M 3.159 0.034 2.536 2.437                                               4 0.10 M 3.159 0.052 2.494 2.416                                               5 0.20 M 3.159 0.072 2.458 2.397                                             ______________________________________                                    

                  TABLE 5                                                          ______________________________________                                         Pulse Train 3 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  2.870    0.000  2.368   2.282                                   2 0.01 M 2.873 0.000 2.372 2.284                                               3 0.05 M 2.878 0.061 2.332 2.299                                               4 0.10 M 2.880 0.078 2.300 2.288                                               5 0.20 M 2.877 0.155 2.140 2.244                                             ______________________________________                                    

                  TABLE 6                                                          ______________________________________                                         Pulse Train 4 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  2.601    0.128  2.063   2.172                                   2 0.01 M 2.602 0.000 2.211 2.176                                               3 0.05 M 2.606 0.000 2.245 2.188                                               4 0.10 M 2.605 0.000 2.236 2.174                                               5 0.20 M 2.595 0.000 2.211 2.139                                             ______________________________________                                    

From the above pulse train data, it can be seen that only the group 2 cells did not exhibit any voltage delay in four pulse trains 1 to 4. For cells with higher LiNO₃ concentrations (groups 3, 4 and 5), voltage delay was detected in pulse trains 2 and 3 but not in pulse train 4. For the control cells (group 1), there was no voltage delay in pulse trains 1 to 3. However, in pulse train 4, voltage delay was only presented in the control cells. In addition, the groups 2, 3 and 4 cells always had their pulse 4 minimum potentials similar or higher than that of the control cells.

                  TABLE 7                                                          ______________________________________                                         Pulse Train 5 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  2.540    0.163  1.672   1.865                                   2 0.01 M 2.539 0.000 2.131 2.069                                               3 0.05 M 2.537 0.000 2.175 2.099                                               4 0.10 M 2.537 0.000 2.157 2.083                                               5 0.20 M 2.536 0.000 2.123 2.056                                             ______________________________________                                    

                  TABLE 8                                                          ______________________________________                                         Pulse Train 6 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  2.505    0.017  1.708   1.745                                   2 0.01 M 2.504 0.000 1.996 1.946                                               3 0.05 M 2.505 0.001 2.080 2.019                                               4 0.10 M 2.503 0.000 2.046 1.987                                               5 0.20 M 2.501 0.000 2.028 1.982                                             ______________________________________                                    

                  TABLE 9                                                          ______________________________________                                         Pulse Train 7 Voltages (average)                                                 Group      [LiNO.sub.3 ]                                                                          Ppre1  V-Delay                                                                               P1min   P4min                               ______________________________________                                         1        0.00 M  2.321    0.000  1.393   1.134                                   2 0.01 M 2.326 0.000 1.494 1.314                                               3 0.05 M 2.350 0.000 1.775 1.489                                               4 0.10 M 2.353 0.000 1.602 1.280                                               5 0.20 M 2.340 0.000 1.650 1.392                                             ______________________________________                                    

Beginning with pulse train 5, all of the cells with LiNO₃ additive exhibited higher pulse 1 minimum and pulse 4 minimum potentials than that of the control cells. The best performance was observed for the group 3 cells with 0.05M LiNO₃ additive. FIGS. 1 to 5 are presented for illustrative purposes to show the contrast in pulse train 5 between the group 1 cells without the LiNO₃ additive and the groups 2 to 5 cells. In particular, curve 10 in FIG. 1 was constructed form the pulse train 5 waveform of a representative group 1 cell devoid of the LiNO₃ additive while curve 20 in FIG. 2 was constructed from the pulse train 5 waveform of a representative group 2 cell activated with the electrolyte having the LiNO₃ additive at a concentration of 0.01M, curve 30 in FIG. 3 was constructed from the pulse train 5 waveform of a representative group 3 cell activated with the nonaqueous electrolyte having the LiNO₃ additive at a concentration of 0.050M, curve 40 in FIG. 4 was constructed from the pulse train 5 waveform of a representative group 4 cell activated with the electrolyte having the LiNO₃ additive at a concentration of 0.10M and curve 50 in FIG. 5 was constructed from the pulse train 5 waveform of a representative group 5 cell activated with the electrolyte having the LiNO₃ additive at a concentration of 0.20M.

The beneficial effect of the lithium nitrate additive in the concentration range of 0.01M to 0.10M is clearly shown in this example. At a higher concentration (0.20M), the additive introduced increased internal resistance into the discharge performance of the cells, probably due to the formation of a thicker anode surface film.

EXAMPLE II

Lithium/silver vanadium oxide cells similar to those discharged in Example I were constructed. The cells were divided into six groups (three cells per group). The cells were activated with the standard electrolyte containing 1.0M LiAsF₆ dissolved in a 50:50, by volume, mixture of PC and DME. The group 1 cells were devoid of a nitrate additive while the groups 2 to 5 cells contained 0.005M, 0.01M, 0.05M, 0.10M and 0.20M of isopropyl nitrate (IPN), respectively.

In a similar manner as the cells discharged in Example I, a constant resistive load of 3.57 kΩ was applied to all of the cells for 21 hours during an initial predischarge burn-in period. Following burn-in, the cells were subjected to acceptance pulse testing consisting of four 10 second pulses (23.2 mA/cm²) with a 15 second rest between each pulse. The averaged discharge readings for the pre-pulse potentials, voltage delay and pulse minimum potentials during acceptance pulse testing for these pulse trains are summarized in Table 10.

                  TABLE 10                                                         ______________________________________                                         Acceptance Pulse Train Voltages (average)                                        Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1      0.00 M    3.262  0.413    2.135 2.508                                     2 0.005 M 3.265 0.288 2.317 2.544                                              3  0.01 M 3.265 0.279 2.308 2.531                                              4  0.05 M 3.257 0.573 1.966 2.495                                              5  0.10 M 3.258 0.634 1.894 2.494                                              6  0.20 M 3.256 0.555 1.969 2.491                                            ______________________________________                                    

In acceptance pulse testing, all groups of cells presented similar pre-pulse potentials and all of the cells exhibited voltage delay. At lower IPN concentrations, the groups 2 and 3 cells exhibited smaller voltage delay than that of the control cells (group 1). Higher pulse 1 and pulse 4 minimum potentials were also observed for the groups 2 and 3 cells relative to the control group. Whereas, at higher IPN concentrations, larger voltage delay and lower pulse minimum potentials were observed for the groups 4 to 6 cells in comparison to the control cells.

Following acceptance pulse testing, all cells were discharged on a 9.53 kohm background load with superimposed pulse trains applied every 39 days. The average discharge readings for the pre-pulse potentials, voltage delay and pulse minimum potentials for pulse trans 1 to 6 are summarized in Tables 11 to 16, respectively.

                  TABLE 11                                                         ______________________________________                                         Pulse Train 1 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1      0.00 M    3.225  0.000    2.601 2.474                                     2 0.005 M 3.225 0.000 2.629 2.520                                              3  0.01 M 3.222 0.000 2.633 2.517                                              4  0.05 M 3.219 0.000 2.602 2.497                                              5  0.10 M 3.219 0.001 2.611 2.498                                              6  0.20 M 3.220 0.000 2.607 2.499                                            ______________________________________                                    

                  TABLE 12                                                         ______________________________________                                         Pulse Train 2 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1      0.00 M    3.168  0.000    2.546 2.406                                     2 0.005 M 3.164 0.000 2.559 2.428                                              3  0.01 M 3.163 0.000 2.546 2.422                                              4  0.05 M 3.165 0.000 2.532 2.394                                              5  0.10 M 3.164 0.000 2.538 2.396                                              6  0.20 M 3.165 0.000 2.536 2.393                                            ______________________________________                                    

                  TABLE 13                                                         ______________________________________                                         Pulse Train 3 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1      0.00 M    2.882  0.000    2.350 2.247                                     2 0.005 M 2.883 0.002 2.362 2.273                                              3  0.01 M 2.882 0.000 2.352 2.261                                              4  0.05 M 2.815 0.000 2.351 2.245                                              5  0.10 M 2.815 0.000 2.344 2.236                                              6  0.20 M 2.818 0.000 2.359 2.256                                            ______________________________________                                    

From the pulse trains 1 to 3 data (Table 11 to 13), it is apparent that none of the cells exhibited voltage delay in any pulse train. For those cells with lower IPN concentrations (groups 2 and 3), higher pulse minimum potentials were observed in all three pulse trains relative to the control cells. However, for cells with higher IPN concentrations (groups 4, 5 and 6), similar pulse minimum potentials were observed relative to the control cells. No detrimental effect from the isopropyl nitrate additive was detected in any of the cell groups.

                  TABLE 14                                                         ______________________________________                                         Pulse Train 4 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1     0.00 M     2.585  0.044    2.096 2.108                                     2 0.005 M  2.591 0.002 2.175 2.142                                             3 0.01 M 2.589 0.001 2.183 2.126                                               4 0.05 M 2.549 0.030 1.922 1.929                                               5 0.10 M 2.564 0.117 1.844 1.886                                               6 0.20 M 2.572 0.064 1.830 1.801                                             ______________________________________                                    

                  TABLE 15                                                         ______________________________________                                         Pulse Train 5 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1     0.00 M     2.525  0.149    1.611 1.791                                     2 0.005 M  2.523 0.026 1.919 1.906                                             3 0.01 M 2.528 0.000 2.077 2.000                                               4 0.05 M 2.500 0.089 1.757 1.753                                               5 0.10 M 2.510 0.040 1.787 1.711                                               6 0.20 M 2.510 0.000 1.804 1.646                                             ______________________________________                                    

                  TABLE 16                                                         ______________________________________                                         Pulse Train 6 Voltages (average)                                                 Group   [IPN]      Ppre1                                                                               V-Delay  P1min P4min                                 ______________________________________                                         1     0.00 M     2.450  0.000    1.684 1.504                                     2 0.005 M  2.449 0.000 1.676 1.575                                             3 0.01 M 2.454 0.000 1.865 1.694                                               4 0.05 M 2.332 0.000 0.778 0.464                                               5 0.10 M 2.364 0.000 0.741 0.412                                               6 0.20 M 2.377 0.000 0.668 0.374                                             ______________________________________                                    

The beneficial effect of isopropyl nitrate additive in the concentration range of 0.005M to 0.01M is clearly shown in the above pulse trains. Higher pulse minimum potentials for the groups 2 and 3 cells were realized than that of the group 1 control cells. At higher concentrations (0.05M to 0.20M), the IPN additive showed no beneficial effect in any pulse train.

FIGS. 6 to 11 are presented for illustrative purposes to show the contrast in pulse train 5 between the group 1 cells without the IPN additive, and the groups 2 to 6 cells. In particular, curve 60 in FIG. 6 was constructed from the pulse train 5 waveform of a representative group 1 cell devoid of the IPN additive while curve 70 in FIG. 7 was constructed from the pulse train 5 waveform of a representative group 2 cell activated with the electrolyte having the IPN additive at a concentration 0.005M, curve 80 in FIG. 8 was constructed from the pulse train 5 waveform of a representative group 3 cell activated with the nonaqueous electrolyte having the IPN additive at a concentration of 0.01M, curve 90 in FIG. 9 was constructed from the pulse train 5 waveform of a representative group 4 cell activated with the electrolyte having the IPN additive at a concentration of 0.05M, curve 100 in FIG. 10 was constructed from the pulse train 5 waveform of a representative group 5 cell activated with the electrolyte having the IPN additive at a concentration of 0.10M and curve 110 in FIG. 11 was constructed from the pulse train 5 waveform of a representative group 6 cell activated with the electrolyte having the IPN additive at a concentration of 0.20M.

The data in Tables 2 to 16 demonstrate the beneficial effects that LiNO₃ and IPN have on increased discharge voltages and improved voltage delay in a pulse discharging electrochemical cell. More generally, however, a nitrate additive according to the present invention should contain an activated R--O bond. While not intended to be bound by any particular theory, it is believed that the formation of Li--O--N(═O)₂ or its reaction products deposited on the anode surface is responsible for the improved performance of an alkali metal/transition metal oxide cell, and in particular Li/SVO cells. If the R group in the nitrate additive is activated (LiNO₃ or IPN for example), the O--R bond is relatively weak. During reduction, the O--R bond breaks to form a product containing the N--O--Li salt group. This is believed to be the reason for the observed improvements in the pulse discharge performance of Li/SVO cells, as exemplified by those having the additives described in Examples I and II.

The concentration limit for the LiNO₃ additive is preferably about 0.01M to about 0.10M while the concentration limit for the IPN additive is preferably about 0.005M to about 0.01M. Cells with those additive concentrations generally presented similar or higher pulse minimum potentials than that of the control cells throughout the respective pulse trains. Generally, the beneficial effect of a nitrate additive will not be apparent if the concentration is less than about 0.001M. On the other hand, if the nitrate additive is at a concentration greater than about 0.20M, the beneficial effect will be cancelled by the detrimental effect of higher internal cell resistance due to the thicker anode surface film formation and lower electrolyte conductivity. This detrimental effect manifests as lower pre-pulse potentials and lower pulse minimum potentials.

Thus, the existence of voltage delay is due to the formation of an anode surface passivation layer that is ionically less conductive than either the anode material itself or the electrolyte solution. In the presence of an alkali metal nitrate, alkaline earth metal nitrate and/or an organic alkyl nitrate additive according to the present invention at a concentration of about 0.005M to about 0.20M, the anode passivation layer is chemically modified to be ionically more conductive than the passivation layer formed without the benefit of the additive. It is believed that due to the presence of the [--O--N(═O)₂ ] functional group, the reductive cleavage of the RO bond in the nitrate additives of the present invention may produce lithium nitrate or the lithium salt of a nitrate reduction product on the anode surface. This surface film is ionically more conductive than the film formed in the absence of the additives and it is responsible for the increased cell performance, especially during pulse discharge applications. As a consequence, higher pulse minimum potentials result when an alkali metal/transition metal oxide couple activated with a nonaqueous organic solvent having a nitrate additive dissolved therein according to the present invention is subjected to a pulse discharge application. This is particularly important in implantable medical devices powered by a cell according to the present invention.

It is appreciated that various modifications to the inventive concepts described herein may be apparent to those of ordinary skill in the art without departing from the spirit and scope of the present invention as defined by the appended claims. 

What is claimed is:
 1. An electrochemical cell, which comprises:a) an anode comprising an alkali metal; b) a solid cathode of electrically conductive material; and c) a nonaqueous electrolyte activating the anode and the cathode, the nonaqueous electrolyte comprising:i) a nitrate additive having the formula: (RO)N(═O)₂, wherein R is an organic group of either a saturated or unsaturated hydrocarbon or heteroatom group containing 1 to 10 carbon atoms; and ii) an alkali metal salt dissolved therein.
 2. The electrochemical cell of claim 1 wherein the nonaqueous electrolyte comprises a first solvent selected from the group consisting of an ester, an ether and a dialkyl carbonate, and mixtures thereof.
 3. The electrochemical cell of claim 2 wherein the first solvent is selected from the group consisting of tetrahydrofuran, methyl acetate, diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane, 1,2-diethoxyethane, 1-ethoxy,2-methoxyethane, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethyl methyl carbonate, methyl propyl carbonate and ethyl propyl carbonate, and mixtures thereof.
 4. The electrochemical cell of claim 2 wherein the nonaqueous electrolyte comprises a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester and a cyclic amide, and mixtures thereof.
 5. The electrochemical cell of claim 4 wherein the second solvent is selected from the group consisting of propylene carbonate, ethylene carbonate, butylene carbonate, acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-butyrolactone and N-methyl-pyrrolidinone, and mixtures thereof.
 6. The electrochemical cell of claim 1 wherein the nitrate additive is selected from the group consisting of propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof.
 7. The electrochemical cell of claim 1 wherein the nitrate additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 8. The electrochemical cell of claim 1 wherein the nitrate additive is isopropyl nitrate present in the electrolyte at a concentration up to about 0.01M.
 9. The electrochemical cell of claim 1 wherein the activated anode and cathode provide the electrochemical cell dischargeable to deliver at least one current pulse of an electrical current of a greater amplitude than that of a prepulse current immediately prior to the pulse.
 10. The electrochemical cell of claim 7 wherein there are at least two pulses delivered in succession with or without an open circuit period between the pulses.
 11. The electrochemical cell of claim 7 wherein the current pulse is of about 23.2 mA/cm².
 12. The electrochemical cell of claim 1 wherein the alkali metal salt is selected from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂ CF₃)₃, LiN(SO₂ CF₃)₂, LiSCN, LiO₃ SCF₂ CF₃, LiC₆ F₅ SO₃, LiO₂ CCF₃, LiSO₃ F, LiB(C₆ H₅)₄ and LiCF₃ SO₃, and mixtures thereof.
 13. The electrochemical cell of claim 1 wherein the solid cathode is selected from the group consisting of silver vanadium oxide, copper silver vanadium oxide, manganese dioxide, cobalt oxide, nickel oxide, fluorinated carbon, copper oxide, copper sulfide, iron sulfide, iron disulfide, titanium disulfide and copper vanadium oxide, and mixtures thereof.
 14. The electrochemical cell of claim 1 wherein the anode is comprised of lithium or a lithium-aluminum alloy.
 15. The electrochemical cell of claim 1 wherein the cathode comprises from about 80 to about 99 weight percent of the cathode active material.
 16. The electrochemical cell of claim 1 wherein the cathode further comprises a binder material and a conductive additive.
 17. The electrochemical cell of claim 16 wherein the binder material is a fluoro-resin powder.
 18. The electrochemical cell of claim 16 wherein the conductive additive is selected from the group consisting of carbon, graphite powder and acetylene black and metallic powder selected from the group consisting of titanium, aluminum, nickel and stainless steel, and mixtures thereof.
 19. The electrochemical cell of claim 1 wherein the cathode comprises from about 0 to 3 weight percent carbon, about 1 to 5 weight percent of a powder fluoro-resin and about 94 weight percent of the cathode active material.
 20. The electrochemical cell of claim 1 associated with an implantable medical device powered by the cell.
 21. In combination with an implantable medical device requiring at least one current pulse for a medical device operating function, an electrochemical cell which is dischargeable to deliver the current pulse while exhibiting reduced voltage delay, the cell which comprises:d) an anode comprising an alkali metal; e) a solid cathode of electrically conductive material; and f) a nonaqueous electrolyte activating the anode and the cathode, the nonaqueous electrolyte comprising:i) a first solvent selected from the group consisting of an ester, an ether and a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester and a cyclic amide, and mixtures thereof; iii) a nitrate additive having the formula: (RO)N(═O)₂, wherein R is an organic group of either a saturated or unsaturated hydrocarbon or heteroatom group containing 1 to 10 carbon atoms; and iv) an alkali metal salt dissolved therein, wherein the activated anode and cathode provide the electrochemical cell dischargeable to deliver at least one current pulse for the medical device operating function, wherein the current pulse is of an electrical current of a greater amplitude than that of a prepulse current immediately prior to the pulse.
 22. The combination of claim 21 wherein the nitrate additive is selected from the group consisting of propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof.
 23. The combination of claim 21 wherein the nitrate additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 24. The combination of claim 21 wherein there are at least two pulses delivered in succession with or without an open circuit period between the pulses.
 25. A method for providing an electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of:a) providing an anode comprising an alkali metal; b) providing a solid cathode of electrically conductive material; and c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising:i) a first solvent selected from the group consisting of an ester, an ether and a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester and a cyclic amide, and mixtures thereof; iii) a nitrate additive having the formula: (RO)N(═O)₂, wherein R is an organic group of either a saturated or unsaturated hydrocarbon and heteroatom group containing 1 to 10 carbon atoms; and iv) an alkali metal salt dissolved therein.
 26. The method of claim 25 including selecting the nitrate additive is selected from the group consisting of propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof.
 27. The method of claim 25 wherein the nitrate additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 28. The method of claim 25 wherein the nitrate additive is isopropyl nitrate present in the electrolyte at a concentration up to about 0.01M.
 29. The method of claim 25 including discharging the cell to deliver at least one current pulse of an electrical current of a greater amplitude than that of a prepulse current immediately prior to the pulse.
 30. The method of claim 29 including discharging the cell to deliver at least two current pulses in succession with or without an open circuit period between the pulses.
 31. The method of claim 29 wherein the current pulse is of about 23.2 mA/cm².
 32. The method of claim 25 including selecting the first solvent from the group consisting of tetrahydrofuran, methyl acetate, diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane, 1,2-diethoxyethane, 1-ethoxy,2-methoxyethane, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethyl methyl carbonate, methyl propyl carbonate and ethyl propyl carbonate, and mixtures thereof.
 33. The method of claim 25 including selecting the second solvent from the group consisting of propylene carbonate, ethylene carbonate, butylene carbonate, acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-butyrolactone and N-methyl-pyrrolidinone, and mixtures thereof.
 34. The method of claim 25 including selecting the alkali metal salt from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂ CF₃)₃, LiN(SO₂ CF₃)₂, LiSCN, LiO₃ SCF₂ CF₃, LiC₆ F₅ SO₃, LiO₂ CCF₃, LiSO₃ F, LiB(C₆ H₅)₄ and LiCF₃ SO₃, and mixtures thereof.
 35. The method of claim 25 including selecting the solid cathode from the group consisting of silver vanadium oxide, copper silver vanadium oxide, manganese dioxide, cobalt oxide, nickel oxide, fluorinated carbon, copper oxide, copper sulfide, iron sulfide, iron disulfide, titanium disulfide and copper vanadium oxide, and mixtures thereof.
 36. The method of claim 25 including providing the anode comprised of lithium or a lithium-aluminum alloy.
 37. The method of claim 25 including providing the cathode comprising from about 80 to about 99 weight percent of the cathode active material.
 38. The method of claim 25 including providing the cathode further comprising a binder material and a conductive additive.
 39. The method of claim 38 wherein the binder material is a fluoro-resin powder.
 40. The method of claim 38 including selecting the conductive additive from the group consisting of carbon, graphite powder and acetylene black and metallic powder selected from the group consisting of titanium, aluminum, nickel and stainless steel, and mixtures thereof.
 41. The method of claim 25 including providing the cathode comprising from about 0 to 3 weight percent carbon, about 1 to 5 weight percent of a powder fluoro-resin and about 94 weight percent of the cathode active material.
 42. The method of claim 25 including powering an implantable medical device with the electrochemical cell.
 43. A method for reducing voltage delay in a pulse discharging electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of:a) providing an anode comprising an alkali metal; b) providing a cathode including a mixed metal oxide comprised of vanadium oxide and a second metal "SM" selected from the group consisting of Groups IB, IIB, IIIB, IVB, VIB, VIIB and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula SM_(x) V₂ O_(y) wherein 0.30≧x≧2.0 and 4.5≧y≧6.0; c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising:i) a first solvent selected from the group consisting of an ester, an ether and a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester and a cyclic amide, and mixtures thereof; iii) a nitrate additive having the formula: (RO)N(═O)₂, wherein R is an organic group of either a saturated or unsaturated hydrocarbon or heteroatom group containing 1 to 10 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) discharging the cell to deliver at least one current pulse of electrical current of a greater amplitude than that of a prepulse current immediately prior to the pulse.
 44. The method of claim 43 including selecting the nitrate additive is selected from the group consisting of propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof.
 45. The method of claim 41 wherein the nitrate additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 46. A method for reducing voltage delay in a pulse discharging electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of:a) providing an anode comprising an alkali metal; b) providing a cathode including a mixed metal oxide comprised of vanadium oxide and a mixture of copper and a second metal "SM" selected from the group consisting of groups IB, IIB, IIIB, IVB, VIB, VIIB, and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula Cu_(x) SM_(y) V₂ O_(z) wherein 0.01≧x≧1.0, 0.01≧y≧1.0 and 5.01≧z≧6.5; c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising:i) a first solvent selected from the group consisting of an ester, an ether and a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester and a cyclic amide, and mixtures thereof; iii) a nitrate additive having the formula: (RO)N(═O)₂, wherein R is an organic group of either a saturated or unsaturated hydrocarbon or heteroatom group containing 1 to 10 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) discharging the cell to deliver at least one current pulse of an electrical current of a greater amplitude than that of a prepulse current immediately prior to the pulse.
 47. The method of claim 46 including selecting the nitrate additive is selected from the group consisting of propyl nitrate, isopropyl nitrate, butyl nitrate, isobutyl nitrate, t-butyl nitrate, benzyl nitrate and phenyl nitrate, and mixtures thereof.
 48. The method of claim 46 wherein the nitrate additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 49. The method of claim 46 wherein in the general formula x≧y. 